Product: HR Polyether Polyols-MW4800
Description:
Hydroxyl Value (mg KOH/g): 32~36
Acid Number (mg KOH/g)≤ 0.08
Water(%)≤ 0.08
Viscosity at 25℃, mpa·s: 700~1050
Application: 4800MW, semi-rigid and high resilience, integral skin molded foam
Product: HR Polyether Polyols-MW6000( High reactive)
Description:
Hydroxyl Value (mg KOH/g): 26~30
Acid Number (mg KOH/g)≤ 0.08
Water(%)≤ 0.08
Viscosity at 25℃, mpa·s: 1000~1300
Application: 6000MW, high reactive, together with POP may give good mechanical strength, for integral skin molded ISF and RIM
Product: HR Polyether Polyols-MW7000（High reactive)
Description:
Hydroxyl Value (mg KOH/g): 29~33
Acid Number (mg KOH/g)≤ 0.08
Water(%)≤ 0.08
Viscosity at 25℃, mpa·s: 1000~1300
Application: 7000MW, high functionality and high reactive, for slabstock or molded foam
Product: HR Polyether Polyols-MW4800 with high reactive and low unsaturation
Description:
Hydroxyl Value (mg KOH/g): 33~37
Acid Number (mg KOH/g)≤ 0.1
Water(%)≤ 0.1
Viscosity at 25℃, mpa·s: 700~1100
Application: 4800MW, high reactive PPG with low unsaturation which can substitute ZS-1618A
Product: HR Polyether Polyols-MW5000
Description:
Hydroxyl Value (mg KOH/g): 20~24
Acid Number (mg KOH/g)≤ 0.1
Water(%)≤ 0.1
Viscosity at 25℃, mpa·s: N/A
Application: 5000MW, with low unsaturation and more than 80% primary hydroxyl, be suitable for cold cured, high resilient PU flexible, RIM and microcellular elastomer (shoe soles)
Product: HR Polyether Polyols-MW4800 with amine terminated polyol
Description:
Hydroxyl Value (mg KOH/g): 32~35
Acid Number (mg KOH/g)≤ 0.05
Water(%)≤ 0.1
Viscosity at 25℃, mpa·s: 900~1100
Application: 4800MW, amine terminated polyol for slabstock or molded foam, be suitable for TDI, MDI or TDI/MDI blended system. Foaming with little or without amine catalyst, TVOC be effectively decreased.